Printing Porcelain in 3D

3D-printed porcelain cup

This winter, we found out about a kickstarter for new 3D-printable ceramic called Porcelite by Tethon3D. Though we are often skeptical of kickstarters, especially in the 3D printing space, we jumped at the opportunity to start experimenting with this material. We have always loved ceramic as a material and were excited by the prospect of creating 3D-printed ceramic pieces. (In fact, our one and only foray into traditional mass production was making a line of ceramic cups and plates). Our first designs for this new material are porcelain cups that remain cool to the touch due to the intricate, cellular nature of their surface. It took us over a month of experimentation to figure out how to properly print the material, and below we discuss some of its challenges and potentials.


timelapse of 3D printing our cup design in porcelite on a Form 2

3D printing ceramics
This is not the first method to make 3D-printed ceramics. In fact, many people have devised ways to do so. The two most common are extrusion-based printing and powder printing. We first saw extruded ceramics through the project L’artisan Electronique by Unfold. We also worked with a startup called Figulo (now Imergio) in 2010, printing ceramics on a converted ZCorp machine. Shapeways offers “3D-printed” ceramics by printing a mold and using traditional slip casting. However, Porcelite is the first method I am aware of that can print ceramics using Stereolithography, SLA (edit: there are other high end SLA ceramics, but nothing accessible at a consumer level).

This piqued our interest for a number of reasons. The aforementioned 3D-printed methods have a number of constraints and limitations that make it difficult to explore the types of forms we design. Extrusion printing cannot stop and start well, limiting it to coiled forms. Powder printing has a fragile green state before firing and coarse texture that prevents working with intricacy and detail. SLA is one of the smoothest and most detailed 3D printing methods, allowing us to more freely explore the sort of design that excites us: complex, intricate parts that can’t be produced by traditional methods. Additionally, we have Formlabs printers in our studio, so it is something we can experiment with in house.

The main downside is size. The print volume is not very large and must accommodate supports and material shrinkage, leading a maximum height of a little over 5 inches.

Designing a Cellular Cup
We wanted to explore ceramic designs that really required the use of 3D printing and would be nearly impossible to make any other way, even by hand. We were also interested in playing with the idea of double-walled chambers or heat sinks for insulating properties. Our previous cups had played with the same idea using ribbed surface textures, but were quite limited due to the constraints of casting.

We designed a series of cups surrounded by intricate cellular networks. These airy structures remain comfortable to touch even when the cup holds hot liquids. Each cup looks as though it’s sheathed in a frozen foam of bubbles. These shapes are not only be beautiful and functional, but are also self-supporting for the printing and firing processes. (This builds upon some of the techniques we first explored last year with New Balance for 3D-printed shoes.)

 

Prototyping and troubleshooting
This material is still new and experimental, so during the prototyping process we had a number problems and setbacks. We can divide these issues into printing and post processing (firing and glazing). First off, the print quality of the material is quite good. The surfaces are smooth, the parts are strong, and overhangs work well. One of the main problems with the material is separation. The material is essentially a photopolymer mixed with fine ceramic powder, and these two components easily separate when undisturbed. Noticeable separation can start in under an hour. For a 10-20 hour print, that can be quite problematic.

printing porcelite on a Form 2

Settings
Because of the separation, we wanted to use the wiper on the Form 2 to add some agitation and mix each layer. However, the Open Mode that Formlabs has for using experimental materials disables the wiper. To get around this, we use an empty cartridge to spoof a normal Formlabs material, instead of using Open Mode. Because we use an empty cartridge, we have to manually add resin for long prints. Though Tethon recommends using the settings for Grey or Black material, we are currently using the settings for Flexible V2. All our prints so far have used 50 micron layer height.

Build adhesion
Our biggest problems have been with the print falling off during printing both from the build plate and the supports. The material is much heavier and more brittle than normal Formlabs materials. We used a rough sandpaper to add a coarse texture to the build plate to aid in adhesion. We also used the “Fine Tuning” settings to lower the starting position by 0.2mm.

We have also had to use fairly large supports. We have been using supports with a contact size of 0.9-1.2mm because of issues with prints breaking off the supports for long jobs. Luckily, the ease with which supports break means they are also significantly easier to remove after printing compared to other materials.

the surface of our cup before firing
the surface of our cup before firing

Firing
After printing, the pieces are fired in a kiln just like normal ceramics. When fired, all the resin burns out and the ceramic goes through vitrification, forming solid porcelain. This causes the part to shrink around 17.5%. All ceramic shrinks when fired, but normally around 12%, so this is a bit high. The shrinking causes stress in the material while firing, which can lead to cracks forming, depending on the geometry. This is true of all ceramics, but even more so in Porcelite. We especially notice cracks forming along layer lines. Also as with all ceramics, parts will slump in the kiln causing unsupported areas to fall or bow.

The print on the left was fired upside down, leading to a slumped shape. The print on the right has noticeable cracking after firing.
Firing problems. The print on the left was fired upside down, leading to a slumped shape. The print on the right has noticeable cracking after firing.

We have also had problems bubbles forming during firings. This happens when the resin is burned out and turns into gas. Tethon recently posted a new firing schedule (how the temperature changes in the kiln) which addresses most of that issue, though we have found it isn’t completely gone. We post cure the prints in a UV oven for around 2 hours before firing, which also seems to help slightly with the bubble formation. We fire in a small desktop kiln in our spray booth to ventilate the burned off resin.

the surface of our 3D-printed porcelain cup after glazing
the surface of our 3D-printed porcelain cup after glazing

Glazing
The easiest part of the process so far has been glazing. We use a normal glaze that we got at the local arts store, Amaco LG-11. We dilute it slightly and spray it on, applying 4 coats. The glaze covers up any visible layers from printing and imperfections such as small cracks. The surface quality and translucency ends up comparable to traditional ceramics.

the cup has a translucent quality even after being glazed
the cup has a translucent quality even after being glazed

Our Porcelite Print Process

The summary of our current process is:

  • Print at 50 micron resolution with Flexible V2 settings on a Form 2 (no Open Mode)
  • Use 0.9-1.2mm supports
  • Roughen build plate with sandpaper
  • Set Fine Tuning to -0.2mm platform offset (this may depend on your printer)
  • Remove supports
  • Post-cure for 2 hours
  • Fire to cone 3 with Tethon3D firing schedule
  • Glaze and fire as per supplier’s instructions

Special thanks for everyone who has helped us out while we’ve been working with this material: Forrest Snyder, Max Lobovsky, Tethon3D, and formlabs

Want to check out other interesting 3D printed ceramic things?
L’artisan ElectroniqueJenny sabin, open 3dp, potterbot, emerging objects

You Might Also Like

  1. Yao

    Thank you very much for this detailed story! Very interesting and readable blog post.

  2. 3D Printing Models STL

    I know pretty much about printing on PLA filament, but never thought of printing on porcelain can be possible. You have detailed this subject in such a way that even an ignorant as me knows how to printing on porcelain should be done and how to make it a trouble less process. Great article, indeed.

  3. Jenn Hoff

    Wow, this is so beautiful! I had to google 3D printed porcelain after seeing Ryan Barrett mention it. I love this beautiful cup! Thank you for the instructions!